PET chips
 

POLYPROPYLENE PP 1550J(T30S)

Product obtainer by polymerization of propylene in presence of comeplex metalorganic catalysts.   Chemical name: Propylene homopolymer
It incorporates increased long-term thermal stability,   Empirical formula:
[-CH2CH(CH3)-]n
thermal-oxidative degradation resistance when PP is produced,processed and PP-made artides are exploited.   Technical requirements:
TU 2211-136-05766801-206

Application:film thread for bags,packing rope and string.

QUALITY

VALUE

TEST METHOD

Flow-melt index(at 2.16 kg/ 230≧),g/10min,in the range

2.9-3.5

ASTM D 1238/L

2.Flexural modulus,MPA,min.

1400

ASTM D 790

3.Tensile strength at yield point,MPa,min

34

ASTM D 638

4.Elongation at yield point,%,min

10

ASTM D 638

5.Gel content,pcs/m2,not more,sizing:
−2.5mm
(1.5-2.5)mm
(017-1.5)mm
−0.2mm


0
3
50
500

P4.8 TU 2211-136-
05766801-2006


Additional reference ratings

QUALITY

VALUE

1.Density,kg/m3

900

2.Packed density of pellets,kg/m3

480-520

3.Mass fraction of ash.%

0.025-0.050

4.Thermal-oxidative aging resistance at 150≧,h

360

5.Vicat softening point in liquid medium under force 10 H, ≧

150-154

6.Thermal creep temperature at load 0.46 H/mO, ≧

90-96

7.Rockwell hardness,R

82-95

POLYETHYLENE PE 6148C(486H3)

Product obtained by gas thase polymerization of ethylene in polyethylene (HDPE)   PE grade: High density
presence of complex metalorganic catalysts.Stabilization recipe: antacid, antioxidant, thermostabilizer,   Chemical name:Ethylene and hexane-1 copoly(-CH2-CH2-)n
Processing aid, dispersing afent. Application:high strength blown film for thin bags.   Design specification:TU 2211-145-05766801-2008

PROPERTY

VALUE

TEST METHOD

1.Density(of base resin),g/cm3 ,in the range

0.946-0.950

ASTM D 1505

Melt Flow Rate,g/10 min,in the range:-at 5..0kg/190≧
-at 2.16kg/190≧

0.25-0.4

TASM D 1238/L

Ratio:
-MFR21.6kg/MFR5.0kg
-MFR21.6kg/MFR21.6kg

Min18

ASTM D 1238


Additional reference Properties

Property

Value

Test Method

1.Dart impact strength,g,min

200

ASTM D 1709

2,Tensile Modulus,2%sec.,MPa,min.:
MD
TD


700
650

ASTM D 882

3.Tensile strength,MPa,min.:
MD
TD


53
50

ASTM D 882

Elongation at break,%,min.:
MD
TD


500
650

ASTM D 882

Elmendorftear strength,min.:
MD
TD


18
55

ASTM D 1922

6.Gel content,pcs./O,max

600

p.6 Attachmet A TU
2211-145-05766801

POLYETHYLENE PE 625J(526F2)

Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.   PE grade: High density polyethylene(HDPE)
Stabilization recipe:antacid,antioxidant,thermostabilizer,processing aid,dispersing agent.   Chenmical name:Ethylene and hexane-1 Copolymer
Empirical formula:(-CH2-CH2-)n
Application:general purpose grade;blow molding of articles up to 2 dm3.  
Design specification:TU 2211-145-
05766801-2008

PROPERTY

VALUE

TEST METHOD

1.Density(of base resin),g/cm3,in the range

0.950-0.954

ASTM D 1505

2.Melt Flow Rate,g/10 min,in the range:
-at 5.0kg/190≧
-at 2.13kg/190≧

0.15-0.3

ASTM D 1238/L

3. Ratio:
-MFR21.6kg/MFR5.0kg
-MFR21.6kg/MFR21.6kg

Above 70

ASTM D 1238


Additional Reference Properties

Property

VALUE

TEST METHOD

1.Flexural Modulus,MPa,min.:

1250

ASTM D 790

2.Lzod Impact Strength at 23≧,J/m,min.:

200

ASTM D 256

POLYETHYLENE PE 6948C(486H3)

Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.   PE grade: High density polyethylene(HDPE)
Stabilization recipe:antacid,antioxidant,thermostabilizer,processing aid,dispersing agent.   Chenmical name:Ethylene and hexane-1 Copolymer Empirical formula:(-CH2-CH2-)n
Application:bsic component for PE 100 class pressure pipers   Design specification:TU 2211-145-05766801-2008

PROPERTY

VALUE

TEST METHOD

1.Density(of base resin),g/cm3,in the range

0.946-0.950

ASTM D 1505

2.Melt Flow Rate,g/10 min,in the range:
-at 5.0kg/190≧
-at 2.13kg/190≧

0.25-0.4

ASTM D 1238/L

3. Ratio:
-MFR21.6kg/MFR5.0kg
-MFR21.6kg/MFR21.6kg

Min 18

ASTM D 1238


Additional Reference Properties

Property

VALUE

Test Method

1.Flexural Modulus,MPa,min.:

1000

ASTM D 790

2.Lzod Impact Strength at 23≧,J/m,min.:

400

ASTM D 256

3.ESCR,hr.

Above 1000

ASTM D 1693

POLYETHYLENE PE 5118Q(18403)

Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.   PE TYPE: High density polyethylene(LLDPE)
Stabilization recipe:antacid,antioxidant,thermostabilizer,processing aid,dispersing agent.   Chenmical name:Ethylene and hexane-1 Copolymer
Empirical formula:(-CH2-CH2-)n
Application:high strength stretch film.   Design specification:TU 2211-145-05766801-2008

PROPERTY

VALUE

TEST METHOD

1.Density(of base resin),g/cm3,in the range

0.916-0.920

ASTM D 1505

2.Melt Flow Rate(at 2.16 kg/190≧),g/10
min,in the range:

2.8-3.4

ASTM D 1238/L

3. -MFR21.6kg/MFR21.6kg ratio,max.

30

ASTM D 1238


Additional Reference Properties

Property

Value

Test Method

1.Dart impact strength,g,min

100

ASTM D 1709

2,Tensile Modulus,2%sec.,MPa,min.:
MD
TD


115
120

ASTM D 882

3.Tensile strength,MPa,min.:
MD
TD


53
50

ASTM D 882

Elongation at break,%,min.
MD
TD


500
900

ASTM D 882

Elmendorftear strength,min.:
MD
TD


190
450

ASTM D 1922

6.Gel content,pcs./O,max,sizing:
1 mm
(0.5-1.0)mm
(0.2-0.5)mm
0.2mm(totally)


0
5
245
250

p.6 Attachmet A TU
2211-145-05766801



Supply form: Pellets
Packaging:

Product is packed into polyethyiene or polupropylenebads(one bag net weght25.00
\0.25kg)and bundled on flat pallets with shrink film.Gross weight of a bundle is max 2t.
PP may be packed into soft contaners(big bags) sized for 400-1000kg.
Upon afreement with a customer.PP pellets may be loaded unpacked straight into wagons for pelleted polumer materials and polymer truck-camers,as well as may be delivered in bags by railcars.

Transportation: By all modes of transport.
Storage: Polypropyiene shall be stored in enclosed dry space preventing from direct sun rays,on shelves or pallets at least 5cm from the flocr,and at least 1m from heaters,at temperature max 30≧ and relative humidity max 80%.
Prior to processing bags with polymer shall be kept for at least 12 hrs in production area.
Information contained herein is provided to the best of our knowledge and is considered true on the revision date.This specification does not release a customer from obligation to check the produce as to suitability thereof for the intended application.A producer shall not be liable for any loss and damage that might occur due to use of this information.

 